Table 2

Compilation of reported mineralogical assemblages recovered after annealing of different amorphous starting materials of MgSiO3 composition.

Temperature (K) Starting Material Mineralogya Analytical Methodsb References

Below Tg
723–873 Sol-Gel (OH detected) En IR 1
933 Sol-Gel (precipitation) Fo XRD/IR 2
970 Sol-Gel (precipitation) Fo XRD/IR 2
973 Sol-Gel (xerogel) Fo XRD/TEM/SEM/IR 3
996 Glass powder (5–10 μm) Fo+Trid TEM/SEM/IR/XRD 4
1000 Laser ablation spherules Fo+Trid TEM 4
1000 Smokes Fo IR 5
1000 Sol-Gel (precipitation) Fo XRD/IR 2
Tg ± 20 K
1023 Sol-Gel (xerogel) Fo+En XRD/IR/SEM 6
1030 Glass powder (5–10 μm) Oen TEM 4
1033 Glass powder (5–10 μm) Fo+Cen+Oen XRD/TEM 3
1053 Sol-Gel (xerogel) Fo+ En XRD/IR/SEM 6
1060 Glass powder (5–10 μm) Oen TEM 4
1063 Sol-Gel (xerogel) Fo+En XRD/IR 6
Above Tg
1073 Laser ablation spherules En SEM/IR 7
1073 Sol-Gel (xerogel) Fo+En XRD/IR 6
1080 Glass chips (100–130 μm) Oen IR/TEM/SEM/XRD 4
1080 Glass powder (5–10 μm) Oen TEM 4
1109 Sol-Gel (spray-drying) Fo+Cen+Oen XRD/DSC 8
1121 Glass chips (100–130 μm) Oen IR/TEM/SEM/XRD 4
1121 Glass powder (5–10 μm) Oen TEM 4
1165 Glass chips (100–130 μm) Oen IR/TEM 4
1173 Geopolymers Fo + Oen XRD/DTA 9
1173 Sol-Gel (precipitation) Cen+Oen XRD/DSC 8
1200 Smoke Fo+Silica IR 5
1273 Sol-Gel (xerogel) Fo+Cen+Oen+Silica XRD/TEM 3
1273 Laser ablation spherules En SEM/IR 7
1273 Sol-Gel (xerogel) Cen+Oen XRD/DTA 10

References. (1) Jäger et al. (2003); (2) Thompson et al. (2002); (3) Roskosz et al. (2009); (4) Fabian et al. (2000); (5) Hallenbeck & Nuth (1998); (6) Murata et al. (2009); (7) Brucato et al. (1999); (8) Douy (2002); (9) Van Long (2008); (10) Maliavski et al. (1997).

Notes.

(a)

Fo: forsterite; Trid: tridymite; En: enstatite (no distinctions between polymorphs); Oen: orthoenstatite; Cen: clinoenstatite; Cr: cristobalite.

(b)

XRD: X-ray diffraction; IR: infra-red spectroscopy; TEM: transmission electron microscopy; SEM: scanning electron microscopy; DSC: differential scanning calorimetry; DTA: differential thermal analysis.

Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.

Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.

Initial download of the metrics may take a while.