Table 1

Experimental conditions and mass of run products.

(1) Exp. Plasma Plasma Pressure (2) Feeding Weight of run product (mg)

no. forming gas flame (KPa) rate Upper Lower Quenching Total value
(L min−1) flow (mg min−1) wall wall part (kPa⋅mg min−1)
Ar 30
(3)MS-1 He 2.5 Tangential 33 61 797.3 212.4 203.5 1213.2 564
O2 0.5
Ar 30
MS-2 He 2.5 Tangential 30 68 1092 171 89 1352 570
O2 0.5
Ar 30
MS-3 He 2.5 Tangential 30 57 907.8 115 113.8 1136.6 493
O2 0.5
Ar 30
MS-4 He 2.5 Tangential 50 18 322.3 40.4 3 365.7 293
O2 0.5
Ar 30
MS-5 He 2.5 Tangential 70 39 648.4 112.3 20.7 781.4 731
O2 0.5
Ar 30
MS-6 He 2.5 Radial 72 35 174.8 414.8 108 697.6 681
O2 0.5

CI-1 Ar 30 Tangential 30 174 3280 198 3478 1253
He 2.5 (mixed)
CI-2 Ar 30 Tangential 70 71 1100.3 160.8 150 1411.1 1197
He 5.0
CI-3 Ar 30 Radial 70 3 14.1 46.9 8.7 69.7 98
He 5.0

Notes. (1) The MS-1 to MS-6 experiments were performed in system MgO-SiO2, and the CI-1 to CI-3 experiments were performed in system Si–Mg–Fe–Na–Al–Ca–Ni–O. (2) Starting materials were injected with argon carrier gas at 3 L min−1. (3) Oxygen slit gas (O2) was additionally injected at 20 L min−1.

Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.

Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.

Initial download of the metrics may take a while.